Long-term thermal ageing of the 2219-T851 and the 2050-T84 Al-Cu alloys

Abstract : In this study, the influence of high temperature exposure on mechanical properties as well as on the microstructures of two Al-Cu alloys, has been investigated. Driven by an industrial will to use structural aluminium at higher temperature than usually stated, this work is focused on the characterization of the evolution of two commercial alloys, the 2219-T851 and the 2050-T84, induced by an ageing treatment of 1000 hours at 200°C. Careful TEM observations confirm the importance of the nanoscale precipitation and that the precipitate size and distribution strongly influence the mechanical properties of the studied alloys. Results unexpectedly show that the precipitates are more stable in time than the precipitates at this temperature. Regarding the mechanical properties related to ageing, it follows that the 2219-T851 alloy presents a reduced drop with time of its tensile test curves compared to the 2050-T84, thus a limited, and at least less pronounced, temperature dependence. For an industrial application on structural part, 2219-T851 alloy then appears to be a good candidate for long-term structural applications at intermediate temperatures.
Complete list of metadata

https://hal.archives-ouvertes.fr/hal-03383476
Contributor : Nicolas Bello Connect in order to contact the contributor
Submitted on : Monday, October 18, 2021 - 3:52:16 PM
Last modification on : Tuesday, October 19, 2021 - 11:18:16 PM

Files

LTTA of the 2219-T851 and the ...
Files produced by the author(s)

Identifiers

Citation

Nicolas Bello, Céline Larignon, Joël Douin. Long-term thermal ageing of the 2219-T851 and the 2050-T84 Al-Cu alloys. Materials Today Communications, Elsevier, 2021, pp.102834. ⟨10.1016/j.mtcomm.2021.102834⟩. ⟨hal-03383476⟩

Share

Metrics

Record views

17

Files downloads

23