Gas barrier and adhesion of interpenetrating polymer networks based on poly(diurethane bismethacrylate) and different epoxy–amine networks - Université Pierre et Marie Curie Accéder directement au contenu
Article Dans Une Revue European Polymer Journal Année : 2002

Gas barrier and adhesion of interpenetrating polymer networks based on poly(diurethane bismethacrylate) and different epoxy–amine networks

V Simic
Laurent Bouteiller
L Gallez
  • Fonction : Auteur
P Merlin
  • Fonction : Auteur

Résumé

Interpenetrating polymer networks (IPNs) composed of poly(methacrylate) and epoxy-amine networks made in situ between two oriented polypropylene sheets were examined in terms of their oxygen barrier and adhesion to the substrate properties. A particular attention was devoted to a system presenting an obvious phase separation in order to establish a correlation between IPN morphologies and gas barrier properties. Kinetics of formation and phase behavior were investigated by infrared and UV-visible spectroscopy, respectively. Since the poly(methacrylate) network could be instantaneously generated by photoirradiation, IPNs differing in network sequence formation were prepared : by varying the moment of irradiation a difference in IPNs structure was expected. Oxygen transmission rates (OTR) of different films irradiated before and after demixion were measured. It was shown that similar OTR are obtained whatever the moment of irradiation.
Fichier principal
Vignette du fichier
Publi Post-pdf version definitive.pdf (479.69 Ko) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)

Dates et versions

hal-01696757 , version 1 (25-01-2023)

Identifiants

Citer

V Simic, S Boileau, Laurent Bouteiller, L Gallez, P Merlin. Gas barrier and adhesion of interpenetrating polymer networks based on poly(diurethane bismethacrylate) and different epoxy–amine networks. European Polymer Journal, 2002, 38 (12), pp.2449--2458. ⟨10.1016/S0014-3057(02)00164-7⟩. ⟨hal-01696757⟩
50 Consultations
7 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More