Textural and phase stability of CexZr1−xO2 mixed oxides under high temperature oxidising conditions

Abstract : The textural and structural changes in several Ce-Zr mixed oxides were studied. Changes in the crystal size and specific surface area upon calcination were followed at 1223 K over time. Different gas compositions (O2, CO2 and H2O) were employed during calcination in order to better understand the sintering process in the CexZr1−xO2 system. From SBET and mean crystal size (D) curves, we have tried to obtain the kinetic parameters. In order to do that, all curves were fitted using a mathematical expression which allows the derivative and then the kinetic rates for SBET decrease and D increase with calcination time to be obtained. It was also possible to correlate these rates with the Ce content of the mixed oxide, and to obtain information about the influence of composition on the sintering process at the surface and the crystalline structure of the mixed oxides. Complementary HREM/TEM data are also presented. With the help of this technique, it has been possible to elucidate the morphological and crystallographic changes in the crystallites upon calcination of the samples under oxidising atmospheres
Type de document :
Article dans une revue
Catalysis Today, 1999, 50 (2), pp.271-284. 〈10.1016/S0920-5861(98)00509-4〉
Liste complète des métadonnées

https://hal-emse.ccsd.cnrs.fr/emse-00609921
Contributeur : Andrée-Aimée Toucas <>
Soumis le : mercredi 20 juillet 2011 - 15:03:08
Dernière modification le : jeudi 11 janvier 2018 - 06:21:23

Lien texte intégral

Identifiants

Citation

Gerardo Colon, Michèle Pijolat, Françoise Valdivieso, Richard Baker, Serafin Bernal, et al.. Textural and phase stability of CexZr1−xO2 mixed oxides under high temperature oxidising conditions. Catalysis Today, 1999, 50 (2), pp.271-284. 〈10.1016/S0920-5861(98)00509-4〉. 〈emse-00609921〉

Partager

Métriques

Consultations de la notice

50