Redox behavior of CeO2-ZrO2 mixed oxides: II. Influence of redox treatments on low surface area catalysts

Abstract : Redox and textural/structural properties of low surface area (LS) ceria-zirconia mixed oxides with composition ranging from 0 to 85 mol% of ZrO2, have been studied using Raman spectroscopy, X-ray diffraction, textural characterization, magnetic susceptibility measurements, temperature-programmed reduction and oxidation and buffering measurements. Special attention was given to the effects of aging under redox conditions. Correlation between chemical composition, textural, structural and redox properties of the oxides is reported. Comparison with previously reported high surface area (HS) samples shows that in spite of the initial low surface area of the present samples (≈20 versus ≈100 m2g−1), the reduction occurs at fairly low temperatures when zirconium is incorporated into the CeO2 lattice. Remarkably, the favorable effects of the redox-aging on the reduction behavior are more pronounced in the present LS samples compared to the previously investigated HS ones. Raman and X-ray investigations revealed that important modifications of the structure take place as a consequence of the redox aging, leading to appreciable CeO2 segregation, which could suggest some correlation between these parameters.
Document type :
Journal articles
Complete list of metadatas

https://hal-emse.ccsd.cnrs.fr/emse-00610076
Contributor : Andrée-Aimée Toucas <>
Submitted on : Thursday, July 21, 2011 - 9:16:08 AM
Last modification on : Thursday, September 10, 2020 - 10:44:02 AM

Links full text

Identifiers

Citation

Hilario Vidal, Jan Kaspar, Michèle Pijolat, Gerardo Colon, Serafin Bernal, et al.. Redox behavior of CeO2-ZrO2 mixed oxides: II. Influence of redox treatments on low surface area catalysts. Applied Catalysis B: Environmental, Elsevier, 2001, 30 (1-2), pp.75-85. ⟨10.1016/S0926-3373(00)00221-6⟩. ⟨emse-00610076⟩

Share

Metrics

Record views

211