Hydrogen effect on dislocation nucleation in a ferritic alloy Fe-15Cr as observed per nanoindentation - Mines Saint-Étienne
Journal Articles Materials Science and Engineering: A Year : 2014

Hydrogen effect on dislocation nucleation in a ferritic alloy Fe-15Cr as observed per nanoindentation

Gaspard Vincent
  • Function : Author
  • PersonId : 956084
Guillaume Kermouche
Connectez-vous pour contacter l'auteur
David Delafosse
Afrooz Barnoush
  • Function : Author
  • PersonId : 956085

Abstract

Hydrogen effects on dislocation nucleation in polycrystalline ferritic Fe-15Cr binary alloy were investigated using in situ electrochemical nanoindentation. Linear elastic finite element calculations taking account of the cubic symmetry of BCC crystals were made to extract the resolved shear stresses on the different slip systems of the indented grains. It is shown that the resolved shear stresses corresponding to the experimentally measured pop-in loads are compatible with homogeneous dislocation nucleation. The resolved shear stress necessary to nucleate dislocations from defect-free crystals was estimated at μ/12-μ/13 without hydrogen. Cathodically charged hydrogen reduces the shear strength of the crystal by 8.5%-19.8%, thus promoting dislocation multiplication.

Domains

Materials
Fichier principal
Vignette du fichier
Gaspard2014.pdf (397.9 Ko) Télécharger le fichier
Origin Files produced by the author(s)

Dates and versions

emse-00989488 , version 1 (20-06-2022)

Identifiers

Cite

Gaspard Vincent, Guillaume Kermouche, David Delafosse, Afrooz Barnoush. Hydrogen effect on dislocation nucleation in a ferritic alloy Fe-15Cr as observed per nanoindentation. Materials Science and Engineering: A, 2014, 604, pp.86-91. ⟨10.1016/j.msea.2014.02.041⟩. ⟨emse-00989488⟩
162 View
74 Download

Altmetric

Share

More