B-type carbonated hydroxyapatite (C_BHA) is potentially an excellent biodegradable bioceramic for bone repair. However, conventional sintering results in formation of undesired phases. Therefore, microwave sintering of C_BHA was investigated to assess the possibility to reduce formation of unwanted phases. Pellets with 0.8 mol% of B-type carbonate were sintered in a multimode instrumented cavity under static air with short thermal cycles. They were prepared from a C_BHA powder alone and from a mixture of C_BHA and carbon powder to generate a local in-situ CO₂ atmosphere. XRD, FT-IR, SEM and BET analyses indicated that C_BHA densification with increase temperature lead to decomposition into apatite. The addition of carbon powder to the C_BHA that generate a CO₂-rich atmosphere around the samples did not prevent the decomposition. Efficient control of temperature and atmosphere composition is required to improve microwave sintering of C_BHA bioceramics.