The Characterization of the oxide films formed at the surface of Ni-base alloys in pressurized water reactors primary coolant by transmission electron microscopy - Mines Saint-Étienne
Conference Papers Year : 2008

The Characterization of the oxide films formed at the surface of Ni-base alloys in pressurized water reactors primary coolant by transmission electron microscopy

Abstract

The oxide film formed on nickel-based alloys in Pressurized Water Reactors (PWR) primary coolant conditions (325°C, aqueous media) has been investigated by Transmission Electron Microscopy (TEM). TEM observations revealed an oxide layer divided in two parts. The internal layer was mainly composed of a continuous spinel layer, identified as a mixed iron and nickel chromite (Ni(1-x)FexCr2O4). Moreover, nodules of Cr2O3 were present at the interface between this spinel and the alloy. The external layer is composed of large crystallites corresponding to a spinel structure rich in iron (Ni(1-z)Fe(2+z)O4) resulting from precipitation phenomena. The influence of alloy surface defects was also studied underlining two main consequences on the formation of the passive film e.g. the internal layer. On one hand, the growth kinetics of the internal spinel rich in chromium increased with the surface defect density. Besides that, when the defect density increased, the oxide scale became more finely crystallized. This result agrees with a growth mechanism due to a rate limiting process of diffusion through the grain boundaries of the oxide. On the other hand, the quantity of Cr2O3 nodules increased with the number of surface defects, revealing that the nodules nucleated preferentially at defect location.
Fichier principal
Vignette du fichier
MP-MSF-595-598-539-orig.pdf (4.54 Mo) Télécharger le fichier
Origin Files produced by the author(s)
Loading...

Dates and versions

emse-00590705 , version 1 (05-05-2011)

Identifiers

Cite

Mohamed Sennour, Loic Marchetti, Stéphane Perrin, Régine Molins, Michèle Pijolat, et al.. The Characterization of the oxide films formed at the surface of Ni-base alloys in pressurized water reactors primary coolant by transmission electron microscopy. 7th International Symposium on High Temperature Corrosion and Protection of Materials, May 2008, Les Embiez, France. pp.539-547, ⟨10.4028/www.scientific.net/MSF.595-598.539⟩. ⟨emse-00590705⟩
219 View
482 Download

Altmetric

Share

More