Use of thermodynamic chemical potential diagrams (µCaO, µCO2) to understand the weathering of cement by a slightly carbonated water
Abstract
Cement is a ubiquitous material that may suffer hazardous weathering. The chemical weathering of cement in natural environment is mostly characterized by the leaching of CaO and the addition of CO2. The different weathering zones that develop at the expense of the cement may be predicted by the help of chemical potential phase diagrams; these diagrams simulate the behaviour of systems open to some chemical elements. Some components have a so-called inert status, that is to say the system is closed for these components, their amount in the system remains constant; some other components have a mobile status, that is to say these components can be exchanged with the outside of the system, their amount can vary from one sample zone to another. The mobile components are represented in the model by their chemical potentials (linked to their concentrations) that are variable in the external environment. The main features of the weathering of a cement system open to CaO and CO2 are predicted in a phase diagram with µCaO et µCO2 as diagram axes. From core to rim, one observes the disappearance of portlandite, ettringite and calcium monosulfoaluminate, the precipitation of calcite and amorphous silica, the modification of the composition of the CSH minerals (hydrated calcium silicates) that see a decrease of their c/s ratio (CaO/SiO2) from the core to the rim of the sample. For the CSH minerals, we have separated their continuous solid solution into three compositions defined by different CaO/SiO2 ratios and called phases 1, 2 and 3: CaO = 0.8, 1.1, 1.8 respectively for one mole of SiO2 knowing that H2O varies in the three compositions.